PHASE II REPORT - Caltrans

More documents

Recommendations

Info

CEL#: 10-17749 1)apply tack coat to disc and break emulsion Project Name: Slurry/Micro Mix Design 2)record weight of specimen after cure, before soaking Aggregate: Type 3 Emulsion: MSE LMCQS-1h 3)cover test specimen with water Source: Table Mtn Source: VSS Emultech 4)abrade for 60 sec Emulsion mid-range target: 11.0 5)rinse debris with 1000ml of water M2 Pre-wet water mid-range target: 14.0 6)carefully pat dry with towel 4 Additive mid-range target: 0.0 Additive: cement type 2 7)record weight after test CAT RESULTS FOR ALL MIXES Additive mid-range target: 1.0 Additive: alum.sulf. Additive mid-range target: Additive: Additive mid-range target: Additive: Comments: Curing Conditions: Cohes.Abrasion w/wheels % material weights,g Temperature,°C 15 25 35 -- aggregate 1350.0 agg Temperature,°F 59 77 95 0.0 cement / lime 0.0 cement Other: ___________ Humidity, % 50 90 14.0 water 189.0 water 1.0 alum.sulf. 13.5 alum.sulf. Soaking period before testing 1 minute 1 hour 11.0 emulsion (target) 148.5 emulsion Other: ___________ Compaction w/ roller immediately before testing yes no 203 A Cure Start End Rolled @ Soaking Temp Temp B C=A-B Original Time Clock Temp Temp Clock Humidity end of cure Period of SOAK of SOAK Final Loss Wt, g minutes Time °F °C Time yes / no before test water water Wt, g Wt, g 1743.6 0:30 11:55 78 26 12:25 92 Y 1 min 79 26 1090 653.6 1752.8 0:30 12:10 78 26 12:40 92 NO 1 min 79 26 1114.7 638.1 1849.3 1:00 9:30 77 25 10:30 92 Y 1 min 79 26 1299.6 549.7 1868.1 1:00 8:20 77 25 9:20 92 NO 1 min 79 26 1432.6 435.5 1862.9 3:00 7:50 77 25 10:50 92 Y 1 min 79 26 1571.5 291.4 1877.5 3:00 7:15 77 25 10:15 92 NO 1 min 79 26 1562.3 315.2 1857.1 5:00 6:00 77 25 11:00 92 Y 1 hour 79 26 1718.8 138.3 1899.4 5:00 5:40 77 25 10:40 92 NO 1 hour 79 26 1762.6 136.8
CEL#: 10-17749 1)apply tack coat to disc and break emulsion Project Name: Slurry/Micro Mix Design 2)record weight of specimen after cure, before soaking Aggregate: Type 3 Emulsion: MSE LMCQS-1h 3)cover test specimen with water Source: Table Mtn Source: VSS Emultech 4)abrade for 60 sec Emulsion mid-range target: 11.0 5)rinse debris with 1000ml of water M2 Pre-wet water mid-range target: 14.0 6)carefully pat dry with towel 5 Additive mid-range target: 0.0 Additive: cement type 2 7)record weight after test Additive mid-range target: 1.0 Additive: alum.sulf. Additive mid-range target: Additive: CAT RESULTS FOR ALL MIXES Comments: tests 1-4 done on 10/05; tests 5-8 done on 10/04 Additive mid-range target: Additive: Curing Conditions: Cohes.Abrasion w/wheels % material weights,g Temperature,°C 15 25 35 -- aggregate 1350.0 agg Temperature,°F 59 77 95 0.0 cement / lime 0.0 cement Other: ___________ Humidity, % 50 90 14.0 water 189.0 water 1.0 alum.sulf. 13.5 alum.sulf. Soaking period before testing 1 minute 1 hour 11.0 emulsion (target) 148.5 emulsion Other: ___________ Compaction w/ roller immediately before testing yes no 204 A Cure Start End Rolled @ Soaking Temp Temp B C=A-B Original Time Clock Temp Temp Clock Humidity end of cure Period of SOAK of SOAK Final Loss Wt, g minutes Time °F °C Time yes / no before test water water Wt, g Wt, g 1790.4 0:30 10:35 96 36 11:05 48 Y 1 min 91 33 1332 458.4 1792.2 0:30 10:20 96 36 10:50 48 NO 1 min 92 33 1396.6 395.6 1756.0 1:00 9:45 95 35 10:45 49 Y 1 min 93 34 1360 396.0 1760.1 1:00 9:30 95 35 10:30 49 NO 1 min 92 33 1379.3 380.8 1781.4 3:00 7:15 93 34 10:15 49 Y 1 min 93 34 1544.9 236.5 1769.5 3:00 7:00 93 34 10:00 49 NO 1 min 93 34 1539.6 229.9 1788.5 5:00 6:00 92 33 11:00 49 Y 1 hour 93 34 1592.1 196.4 1748.6 5:00 5:45 92 33 10:45 49 NO 1 hour 93 34 1530.5 218.1
Page 1 and 2:
PHASE II REPORT Slurry Seal / Micro
Page 3 and 4:
CALTRANS Fugro Consultants, Inc. Co
Page 5 and 6:
CALTRANS Fugro Consultants, Inc. Co
Page 7 and 8:
For the Phase II work, the research
Page 9 and 10:
2.0 CHAPTER 2 INTRODUCTION 2.1 BACK
Page 11 and 12:
3.0 Findings from the ruggedness te
Page 13 and 14:
START Test Mix Components Accept Ma
Page 15 and 16:
For all the above considerations, t
Page 17 and 18:
Type II and III microsurfacings are
Page 19 and 20:
“M” Refers to an ASSHTO Standar
Page 21 and 22:
Viscosity: A property of the mix th
Page 23 and 24:
3.6.2 The European Mixing Test Base
Page 25 and 26:
Mix Torque kg-cm 70 60 50 40 30 20
Page 27 and 28:
Clamping Pressure 200Kpa Interface
Page 29 and 30:
Samples Holes 0.8 inches (~0.20 mm
Page 31 and 32:
• Abrasion: CAT. This test may be
Page 33 and 34:
3.7.1 Step 1: Materials Selection T
Page 35 and 36:
3.7.6 Step 6: Evaluate the Long Ter
Page 37 and 38:
4.2 LABORATORY TEST METHODS DEVELOP
Page 39 and 40:
Table 4.2.2: TB-113 Results for Mix
Page 41 and 42:
In addition to the “base mixture
Page 43 and 44:
The resulting mix had the following
Page 45 and 46:
Features: Produces a tangential flo
Page 47 and 48:
Mixing Containers type and size: a.
Page 49 and 50:
• 50 rpm mixing speed This config
Page 51 and 52:
The shape of the traces for differe
Page 53 and 54:
Figure 4.10: Mix M4 Trace with Stan
Page 55 and 56:
The recommended mixing procedure fo
Page 57 and 58:
Figure 4.14: AMT Trace for Mix M1,
Page 59 and 60:
Figure 4.16: Automated Cohesion Tes
Page 61 and 62:
As illustrated in Figures 4.17 and
Page 63 and 64:
Note that the ratio of the two aver
Page 65 and 66:
• Dry Loss Method - Two identical
Page 67 and 68:
Loss (%) 35 30 20 15 10 5 0 Effect
Page 69 and 70:
The differences in the samples were
Page 71 and 72:
Both systems were correctly defined
Page 73 and 74:
Time (Min) Wet Loss M1 (g) Table 4.
Page 75 and 76:
observation. For long term abrasion
Page 77 and 78:
4.3.2 Evaluation of Cohesion-Abrasi
Page 79 and 80:
4.4 REVISED MIX DESIGN METHOD (VERS
Page 81 and 82:
Step 5: Evaluate the Cohesion Prope
Page 83 and 84:
5.0 CHAPTER 5 RUGGEDNESS TESTING 5.
Page 85 and 86:
These levels will be far enough apa
Page 87 and 88:
5.3.3 ACT Test For this test, the c
Page 89 and 90:
6.1.2 AGGREGATE Mineral aggregate s
Page 91 and 92:
shall perform the mix design. The p
Page 93 and 94:
6.5.2 TEST STRIP. With the coordina
Page 95 and 96:
6.6.5 MACHINE CALIBRATION. Each uni
Page 97 and 98:
6.7 METHOD OF MEASUREMENT 6.7.1 ARE
Page 99 and 100:
Delays in the progress of the resea
Page 101 and 102:
2.4 IDA Werke EUROSTAR Power contro
Page 103 and 104:
4.3 If the mix does not break, the
Page 105 and 106:
8.0 PROCEDURE 8.1 Maintain the aggr
Page 107 and 108:
11.2.1.1 BT: brown color transfer t
Page 109 and 110:
Note: Closing all other programs ru
Page 111 and 112:
− Eurostar mixer - the parameter
Page 113 and 114:
Figure A.5: Display of Functional U
Page 115 and 116:
To stop the test, select the drop d
Page 117 and 118:
2.3 ISSA TB-100, Test Method for We
Page 119 and 120:
5.4 Suitable specimen casting mold
Page 121 and 122:
8.2 The amounts of material compone
Page 123 and 124:
9.2 Completely cover the specimen w
Page 125 and 126:
APPENDIX C RESULTS OF RUGGEDNESS AM
Page 127 and 128:
Figure C.2: Ruggedness Trials Trial
Page 129 and 130:
Figure C.4: Ruggedness Trials Trial
Page 131 and 132:
CEL#: 10-17749 LAB #: Date Tested:
Page 133 and 134:
Page 135 and 136:
Page 137 and 138:
Page 139 and 140:
CAT: COHESION ABRASION TEST (FRENCH
Page 141 and 142:
Page 143 and 144:
Page 145 and 146:
Page 147 and 148:
Page 149 and 150:
2.CAT-Cohesion Abrasion Test: Frenc
Page 151 and 152:
GRADATION ANALYSIS FOR AGGREGATE A1
Page 153 and 154:
Page 155 and 156:
Page 157 and 158: GRADATION ANALYSIS FOR AGGREGATE A1
Page 159 and 160: GRADATION ANALYSIS FOR AGGREGATE A1
Page 161 and 162: Source: Lopke (A2) Aggregate: ISSA
Page 171 and 172: GRADATION ANALYSES FOR AGGREGATE A3
Page 181 and 182: SODIUM SULFATE SOUNDNESS FOR AGGREG
Page 183 and 184: SODIUM SULFATE SOUNDNESS FOR AGGREG
Page 185 and 186: ABRASION LOSS BY AASHTO T-96 FOR AG
Page 187 and 188: SAND EQUIVALENT FOR AGGREGATES A1,
Page 189 and 190: ABRASION LOSS BY ASTM D6928 FOR AGG
Page 191 and 192: CEL# 10-17749 Source: Sem Materials
Page 193 and 194: CEL# 10-17749 Source: VSS Emultech
Page 195 and 196: CEL# 10-17749 Source: Ergon Materia
Page 197 and 198: Automated Mixing Test Mix: M3 Agg:
Page 199 and 200: CEL#: 10-17749 1)apply tack coat to
Page 207: CEL#: 10-17749 1)apply tack coat to
Page 229 and 230: Aggregates: Emulsions: Mixes: CAT R
Page 231 and 232: ACT RESULTS FOR ALL MIXES TEST RESU
Page 233 and 234: ACT RESULTS FOR ALL MIXES 228
Page 247 and 248: not effective if placed on pavement
Page 249 and 250: Table F.1: Draft Outline for Refere
Page 251 and 252: David Peshkin will take the lead in
Page 253 and 254: Ride quality has been shown to impa
Page 255 and 256: agency will be held prior to constr
Page 257 and 258: An agency that desires to participa
show all

PHASE II REPORT - Caltrans