21. COMPOSITE SYSTEMS FOR STRUCTURAL STRENGTHENING
MapeWrap B UNI-AX
Unidirectional, high strength basalt
fibre fabric. The fibre is available in two
weights with the same width.
MapeWrap C BI-AX
Balanced, high-strength, bi-directional
carbon fibre fabric.
MapeWrap C Fiocco
Carbon fibre cord to be impregnated
with MAPEWRAP 21 (two-component,
super-fluid epoxy resin).
MapeWrap C
QUADRI-AX
Balanced, high-strength, quadridirectional
carbon fibre fabric.
TECHNICAL DATA:
Weight: 400-600 g/m².
Equivalent thickness of dry fabric: 0.143-0.214 mm.
Tensile strength (N/mm²): > 4.840.
Tensile modulus of elasticity (GPa): 89.
Width: 40 cm.
Elongation at failure: 2%.
Packaging: 50 m rolls.
TECHNICAL DATA:
Weight: 230-360 g/m².
Equivalent thickness of dry fabric: 0.064-0.10 mm.
Tensile strength (MPa): > 4.800, > 4.800.
Tensile modulus of elasticity (GPa): 230-230.
Width: 20-40 cm.
Elongation at failure: 2.1%.
Packaging: 50 m rolls.
TECHNICAL DATA:
Diameters available: 6, 8, 10 and 12 mm.
Equivalent surface area of dry fabric:
diam. 6 mm 15.70 mm²;
diam. 8 mm 21.24 mm²;
diam.10 mm 26.79 mm²;
diam.12 mm 31.40 mm²;
Modulus of elasticity: 230,000 N/mm².
Tensile strength: 4,830 N/mm².
Elongation at failure: 2%.
Packaging: 10 m rolls.
TECHNICAL DATA:
Weight: 380-760 g/m².
Equivalent thickness of dry fabric: 0.053-0.106 mm.
Tensile strength (MPa): > 4.800.
Tensile modulus of elasticity (GPa): 230.
Width: 30-48.5 cm.
Elongation at failure: 2.1%.
Packaging: 50 m rolls.