GENERAL CATALOGUE - Mapei

MapeWrap C UNI-AX
High-strength, unidirectional carbon
fibre fabric with a high modulus of
elasticity (230,000 N/mm²).
A version with a very high modulus
of elasticity (390,000 N/mm²) with the
same weight and width is also available
upon request, called MAPEWRAP C
UNI-AX HM.
MapeWrap G Fiocco
Glass fibre cord to be impregnated
with MAPEWRAP 21 (two-component,
super-fluid epoxy resin).
MapeWrap G
QUADRI-AX
Balanced, quadri-directional glass
fibre fabric.
MapeWrap G UNI-AX
Unidirectional, high strength glass fibre
fabric.
TECHNICAL DATA:
Weight: 300-600 g/m².
Equivalent thickness of dry fabric: 0.166-0.333 mm.
Tensile strength: 4,830 N/mm².
Tensile modulus of elasticity (GPa): 230.
Elongation at failure: 2%.
Width: 10 - 20 - 40 cm.
Packaging: 50 m rolls.
TECHNICAL DATA:
Type of fibre: E type glass.
Diameters available: 6, 8, 10 and 12 mm.
Equivalent surface area of dry fabric:
diam. 6 mm 16.34 mm²;
diam. 8 mm 21.45 mm²;
diam. 10 mm 27.58 mm²;
diam. 12 mm 32.69 mm².
Modulus of elasticity: 80,700 N/mm².
Tensile strength: 2,560 N/mm².
Elongation at failure: > 3%.
Packaging: 10 m rolls.
TECHNICAL DATA:
Type of fibre: E type glass.
Weight: 1140 g/m².
Equivalent thickness of dry fabric: 0.1096 mm.
Tensile strength (MPa): 2,600.
Tensile modulus of elasticity (GPa): 73.
Width: 30-48.5 cm.
Elongation at failure: 3.5-4%.
Packaging: 50 m rolls.
TECHNICAL DATA:
Type of fibre: E type glass.
Weight: 300-900 g/m².
Equivalent thickness of dry fabric: 0.16-0.48 mm.
Tensile strength: 2,560 N/mm².
Tensile modulus of elasticity (GPa): 80.7.
Elongation at failure: 3-4%.
Width: 30-60 cm.
Packaging: 50 m rolls.
167