GENERAL CATALOGUE - Mapei

FIBROstabilitura
FIBROstabilitura is a transpirant
finishing mortar for masonry suitable
for internal and external biocompatible
render without cracks or crazing.
FIBROstabilitura is reinforced with fibres
which guarantee that no shrinkage
cracks or crazing form during drying,
and has unrivalled workability.
FIBROstabilitura is a highly ecological
product which responds fully to the
construction requirements of ecofriendly
building work.
Grassello di CALCE
Aerial binder for transpirant, ecological
finishing compounds and render.
Aerial binder for preparing traditional
masonry render and mortar on site,
the main ingredient for making natural,
transpirant paintwork, final smoothing
coats on render (fresh on fresh) and for
restoring ancient buildings.
HR15
For fire-resistant constructions with high
structural characteristics.
HR15 is a HIGH STRENGTH render
RESISTANT TO FIRE. It Is particularly
suitable for laying concrete and
cement blocks and brickwork and
is also suitable for rendering. It may
be used for protecting and repairing
concrete structures, in compliance
with EN 1504-3.
MALTE
PER INTONACI
CS IV
CONFORME ALLA NORMA
EUROPEA EN 998-1
MaltaBASTARDA
The innovative formulate to make
masonry and render quickly.
Ready-mixed mortar with guaranteed
performance figures for internal and
external render, load-bearing and
partition walls, sealing water pipes and/
or cable runs and for installing shower
troughs and sanitary fittings.
MALTE
PER INTONACI
CS IV
CONFORME ALLA NORMA
EUROPEA EN 998-1
MALTE
PER MURATURA
M15
CONFORME ALLA NORMA
EUROPEA EN 998-2
MALTE
PER MURATURA
M5
CONFORME ALLA NORMA
EUROPEA EN 998-2
EN 459-1
CALCI DA
COSTRUZIONE
CL 90-S PL
CONFORME ALLA NORMA
EUROPEA EN 459-1
EN 998-1
EN 998-2
EN 1504-3
EN 998-1
EN 998-2
TECHNICAL DATA
Mixing ratio: supplied ready to use, may be mixed
when first used if required.
Coefficient of permeability to water vapour: μ = 9.
Composition: slaked lime (type CL 90-S PL), fine
natural silica sand (cat. 0/1 mm) and microfibres.
Yield: approximately 2.0-3.0 kg per square metre per
mm of thickness.
Packaging: 25 kg sacks.
TECHNICAL DATA:
Mixing ratio: the product is supplied ready to use. If
necessary, mix well before use.
Composition: calcium hydroxide [Ca(OH)2].
Yield: approximately 1.5 kg per square metre per mm
of thickness.
Packaging: 25 kg bags.
TECHNICAL DATA:
Fire resistance: REI 180.
Mixing ratio: 1 25 kg bag of HR 15 with approx.
3.5 litres of water.
Mixing time: 3 minutes.
Pot life of mix: 30-40 minutes.
Compressive strength after 28 days: ≥ 15 N/mm².
Yield: 100 kg (4 bags) for approximately 5.5 m² per
mm of thickness or approximately 5 m² of wall with
20x20x40 cm cement blocks.
Packaging: 25 kg bags.
TECHNICAL DATA:
Mixing ratio: 1 25 kg sack of MaltaBASTARDA with
approximately 3.5 litres of water.
Mixing time: 3 minutes.
Pot life of mix: 30-40 minutes.
Compressive strength after 28 days: ≥ 6 N/mm².
Yield: 100 kg (4 bags) for approximately 6 m² per
mm of thickness or approximately 4.5 m² of wall with
12x12x24 cm bricks.
Packaging: 25 kg bags.