SHRP-A-379 traducir

Recommendations

Info

P = Grab Pw (4) where p = unit mass of the compacted slab, kg/m 3 Pw = unit mass of water, kg/m 3 7.6 Determine the mass, M (in kilograms) of the compacted slab: M=pV 7.7 Determine the mass of the aggregate required for compaction as shown below in equations 5 and 6. Equation 5 uses the asphalt content based on the dry mass of the aggregate, whereas equation 6 uses the asphalt content based on total mass of the mixture. M.g : (5) I +%AC I( )] 100 : M [1- %ac] (6) [ loo j where M_r = total mass of aggregate, kg %AC = asphalt content 7.8 Determine the mass of asphalt binder required for compaction as shown in equations 7 and 8 below. Equation 7 uses the asphalt content based on the dry mass of the aggregate, whereas equation 8 uses the asphalt content based on total mass of the mixture. MAC : M,,_ [ %AC] (7) [_J [%AC] (8) MAc : M [_j where M,w = mass of asphalt binder, kg 171
8. REPORT 8.1 The report shall include the following information: 8.1.1 Bituminous Mixture Description--bitumen type, bitumen content, aggregate type, aggregate gradation, and air void percentage. 8.1.2 Mix and compaction temperatures, °C. 8.1.3 Mass of specimen in air, g (A) 8.1.4 Mass of specimen in air with Parafilm, g (B) 8.1.5 Mass of specimen in water with Parafilm, g (C) 8.1.6 Specific gravity of Parafilm (D) 8.1.7 Bulk specific gravity, G,,_, 8.1.8 Maximum specific gravity, G,,_ 8.1.9 Air void content of specimen, percent 8.1.10 Dimensions of mold, cm 8.1.11 Volume of mold, cm3 8.1.12 Unit mass of compacted slab, kg/cm 3 8.1.13 Mass of mix required for compaction, kg 8.1.14 Mass of aggregate required for compaction, M_r (kg) 8.1.15 Weight of asphalt required for compaction, MAc(kg) 8.1.16 Time of mixing, minutes 8.1.17 Time of compaction, minutes 9. PRECISION 9.1 A precision statement has not yet been developed for this test method. 172
Page 1 and 2:
SHR -A-379 The SUPERPAVE Mix Design
Page 3 and 4:
Acknowledgments The research descri
Page 5 and 6:
M-003 Determining the Shear and Sti
Page 7 and 8:
Introduction This volume of the Fin
Page 9 and 10:
Table 2. AASHTO and Other Test Meth
Page 11 and 12:
T48 Method of Test for Flash and Fi
Page 13 and 14:
10. KEY WORDS Asphalt binder, aspha
Page 15 and 16:
Table 1. Performance-Graded Asphalt
Page 17 and 18:
2.2 ASTM Standards: C802 Conducting
Page 19 and 20:
7. APPARATUS 7.1 Bending Beam Rheom
Page 21 and 22:
7.6 Calibrated Thermometers--Calibr
Page 23 and 24:
11.3 Perform a daily quality contro
Page 25 and 26:
NOTE9.--The specified preload on th
Page 27 and 28:
dG d2 --_ I d __
Page 29 and 30:
CO U_ P z_ MLLI L_O° _ _ _c_ r_ j4
Page 31 and 32:
m) _L wO O_ W _Z _W W_ Z w W_ 0 _ w
Page 33 and 34:
1.4 Maximum bending stress--The max
Page 35 and 36:
Sy = log S(8) + log S(15) + ... log
Page 37 and 38:
Z 1.3 1.2 1.1 , , .... J 1 • '; "
Page 39 and 40:
T240 Test Method for Effect of Heat
Page 41 and 42:
5.2 The complex shear modulus is an
Page 43 and 44:
7. HAZARDS 7.1 Standard laboratory
Page 45 and 46:
9.1.1.2.3 A thermocouple probe shal
Page 47 and 48:
Typically, reliable test results ma
Page 49 and 50:
figure 1 can be generated by gradua
Page 51 and 52:
150 "ZERO" STRAIN VALUE O" STRAIN V
Page 53 and 54:
Page 55 and 56:
5.3 For evaluating an asphalt binde
Page 57 and 58:
time. A change in the load signal e
Page 59 and 60:
9.1.1 Load cell--Verify calibration
Page 61 and 62:
11.2 Immediately after demolding, p
Page 63 and 64:
13.1.5 the average failure strain,
Page 65 and 66:
IA A 5,0 I 6 0 86,0 9,5 FILLET O,K.
Page 67 and 68:
--__6_- -_A AL AL _ o 0 _ _ _ "_ f-
Page 69 and 70:
I __;___ i --_'-- :" (_ . /_/Spring
Page 71 and 72:
Page 73 and 74:
points within the pressure vessel a
Page 75 and 76:
NOTE7.--Aging temperature in the PA
Page 77 and 78:
13. KEY WORDS Accelerated aging, el
Page 79 and 80:
to temperaturetransducerand te_llpe
Page 81 and 82:
3. SUMMARY OF METHOD 3.1 The paving
Page 83 and 84:
7. PRECAUTIONS 7.1 Solvents should
Page 85 and 86:
9.4 Final Extraction and Recovery 9
Page 87 and 88:
Glass Wool Plug Figure 2. Extractio
Page 89 and 90:
5.761 in I.D. 6 holes 3/16 in I.D.
Page 91 and 92:
1/4 I.D. 5 3/4 in I.D. 6 holes 5/16
Page 93 and 94:
Polypropylene Cloth Filter I" .....
Page 95 and 96:
114 in I.D. 11 1/4 in I.D. 8 holes
Page 97 and 98:
3. SUMMARY OF TEST METHOD 3.1 A sol
Page 99 and 100:
drying should be re-dried. Caution:
Page 101 and 102:
8.16 Clean the funnels, volumetric
Page 103 and 104:
Adsorption/Desorption Testing Data
Page 105 and 106:
2.3 ASTM Standards: D 4402 Measurem
Page 107 and 108:
5.6.3 Start time of test; 5.6.4 Spe
Page 109 and 110:
9.1.1 Weigh the aggregate fractions
Page 111 and 112:
11. CALCULATIONS AND INTERPRETATION
Page 113 and 114:
3.1 Test System--The test system is
Page 115 and 116:
4.3 Determine Air Void Content--Det
Page 117 and 118:
• vertical displacement of the sp
Page 119 and 120:
The following engineering quantitie
Page 121 and 122:
the axial actuator is under closed
Page 123 and 124:
Figure 2. Platen-Specimen Assembly
Page 125 and 126:
Figure 4. Positioning of Vertical a
Page 127 and 128: tO0 © © ....... OT...=.c on A TEM
Page 129 and 130: Standard Method of Test for Determi
Page 131 and 132: 3. SUMMARY OF METHOD 3.1 This test
Page 133 and 134: 6.5.1 For analog strip-chart record
Page 135 and 136: 8. PROCEDURE 8.1 Measure the bulk s
Page 137 and 138: movement per minute. Both the horiz
Page 139 and 140: If E is greater than 0.01, substitu
Page 141 and 142: Table 1. Correction Factors for Hor
Page 143 and 144: Figure 2. Specimen Loading Frame wi
Page 147 and 148: 6. APPARATUS 6.1 Environmental Cond
Page 149 and 150: 9.3 Heat or cool the asphalt concre
Page 151 and 152: pressed. Otherwise, measure and rec
Page 153 and 154: 10.7.2.3 Apply a repeated axial com
Page 155 and 156: 11.3.1 Peak Stress (kPa) per load c
Page 157 and 158: 12.1.3 Aggregate Type and Gradation
Page 159 and 160: Specimen Temperature Hi/Lo Limit Pr
Page 161 and 162: i Pressure Differential Gauge /_ 0
Page 163 and 164: I0 0 0 0 0 0 0 0 0 Ooo00 0 0 '_,Oo
Page 165 and 166: " Total Elastic 0 Ei._ 0 121 Plasti
Page 167 and 168: T201 Method of Test for Kinematic V
Page 169 and 170: 6.4.4 One metal spatula or spoon 6.
Page 171 and 172: 11.1.1 Asphalt Binder Grade 11.1.2
Page 173 and 174: D 1561-81a Preparation of Bituminou
Page 175 and 176: After filling, close all containers
Page 177: l i /l Gmb = . (1) B-Cwhere A = Mas
Page 181 and 182: 1 RAMP, ..:i!i!iiiii:i:i:i:i:i:i:i:
Page 185 and 186: 3.3 Epoxy Nut to Neutral Axis of Sp
Page 187 and 188: 5.1.6 Cumulative Dissipated Energy
Page 189 and 190: plot 6.1.11 Plot of Dissipated Ener
Page 191 and 192: Figure 2. Nut Epoxied to Neutral Ax
Page 193 and 194: Figure 4. Nut/Block/Screw/LVDT Conn
Page 195 and 196: 0 OO £ m -r"_ mlO 5 10 4 , [ 'T I
Page 197 and 198: As a minimum, the test system, shou
Page 199 and 200: With the ink marker, trace diar_.et
Page 201 and 202: 5. CALCULATIONS A_er the specime_ f
Page 203 and 204: Step Motor L,.._ Loading Rod Swivel
Page 205 and 206: ATHENA TEMPERATURECONTROLLER ii:!i:
Page 207 and 208: Standard Practice for The Laborator
Page 209 and 210: 2.2 SHRP Documents B-006 Extraction
Page 211 and 212: using the same SUPERPAVE ® perform
Page 213 and 214: must be used with the modifier from
Page 215 and 216: 8.2.3 Sections 8.3 and 8.4 present
Page 217 and 218: 8.8.2 Conditioning and Testing--Car
Page 219 and 220: 9. LABORATORY EVALUATION OF AGGREGA
Page 221 and 222: shear, volumetric and frequency swe
Page 223 and 224: 12.2 The HMA plant should produce t
Page 225 and 226: Table 1. Modifier Selection and Cha
Page 227 and 228: Table 5. Guidelines for Binder Modi
Page 229 and 230:
Standard Practice for Grading or Ve
Page 231 and 232:
6. TEST PROCEDURE FOR GRADING AN UN
Page 233 and 234:
7. TEST PROCEDURE FOR VERIFYING THE
Page 235 and 236:
8. REPORT 8.1 If the grade of the a
Page 237 and 238:
1.4 In order to attain adequate pre
Page 239 and 240:
5.4 Calculate the bulk specific gra
Page 241 and 242:
Standard Practice for Measurement o
Page 243 and 244:
Table 1. Test Matrix for Level 2 Mi
Page 245 and 246:
6. SPECIMEN PREPARATION 6.1 All tes
Page 247 and 248:
Record axial deformation, shear def
Page 249 and 250:
7.3.5 Since the specimen will be su
Page 251 and 252:
NOTE 15.--At each temperature, the
Page 253 and 254:
Table 7. Time Estimate for Level 2
Page 255:
NOTEA1.2.--This stress-controlled t