BDG Informationszentrum<br />
Eisengusswerkstoffe<br />
Dokumenten-Nummer: 57817<br />
Tagungsbeitrag<br />
Anjos, Vitor; Silva Ribeiro, Carlos A.; Dias, Fatima; Baumgart, Wolfgang; Cunha, Joao<br />
Publikationssprache: Englisch<br />
Literature Survey on Porosity and Microporosity in Cast Irons Related to Expansion and Gas<br />
Entrapment Phenomena<br />
Literaturübersicht über Porosität und Mikroporosität von Gusseisenwerkstoffen bezogen auf die Ausdehnungs- und<br />
Gasentwicklungsphänomene<br />
Macro and microporosity in castings are a problem that persists at many foundries, despite the use of advance<br />
simulation software's. This fact indicates that other parameters rather then the casting shape/design or the "standard"<br />
metallurgical characteristics are not properly controlled, consi<strong>der</strong>ed or modelled in the solidification simulation. In this<br />
paper we present the Phase I of a research project, which consists on a bibliographic review of the previous attempts to<br />
evaluate the relationship between solidification sequence and the measurement of expansion of molten metal during<br />
eutectic solidification and is relation to porosity and shrinkage defects.<br />
OCC, Mönchengladbach, DE; Universidade do Porto, PT<br />
Erscheinungsjahr 2010<br />
S. S.410-415<br />
Seiten/Bil<strong>der</strong>/Tabellen/Quellen: 6S<br />
Eisengusswerkstoffe<br />
Dokumenten-Nummer: 57875<br />
Tagungsbeitrag<br />
Asenjo, Iker; Lacaze, Jacques; Larranaga, Peio; Mendez, Susana; Sertucha, Jon; Suarez, Ramon<br />
Publikationssprache: Englisch<br />
Microstructure Investigation of Small-Section Nodular Iron Castings with Chunky Graphite<br />
Untersuchung des Mikrogefüges in dünnwandigen Gussteilen aus Gusseisen mit Kugelgraphit mit Chunky-Graphit<br />
Parameters that affect chunky graphite formation in heavy-section castings have been studied in previous works which<br />
showed that inoculation and cerium addition both increase the tendency for this degenerate graphite. This suggested<br />
that laboratory study on chunky graphite formation could be performed on small castings by over-treating the melt.<br />
Though the role of silicon was not ascertained, it appeared of potential interest to also investigate its effect in relation<br />
with the carbon equivalent of the iron and the nucleation potential of the melt. Keel-blocks were thus cast using Ce or<br />
Ce-Mg treated melts, with increased silicon content (up to 4.0 wt.%) and inoculation rate as compared to usual practice.<br />
It was observed that chunky graphite systematically appeared in more or less extended areas centred on the upper part<br />
of the keel-blocks. The as-cast microstructure (graphite shape and distribution) has then been studied in relation to melt<br />
composition and additions (Ce treatment and inoculation) in both affected and non-affected areas. Finally, microanalysis<br />
of oxides and other minor phases showed them to be similar to those appearing in heavy-section castings. It may then<br />
be concluded that chunky graphite appears in light-section castings in the same way than in heavy-section castings<br />
when using over-treated melts.<br />
AZTERLAN - Centro de Investigacion Metallurgica, Durango, ES; CNRS UMR 5085, Centre Interuniversitaire de<br />
Recherche et d'Ingenierie des Materiaux (CIRIMAT), ENSIACET, INPT, Universite Paul Sabatier, Toulouse, FR<br />
Erscheinungsjahr 2010<br />
S. S.52-57<br />
Seiten/Bil<strong>der</strong>/Tabellen/Quellen: 6S<br />
<strong>Giesserei</strong> <strong>Literaturschau</strong>