Megaİzo Kristalize Cement Based, Crystallized Waterproofing Mortar Resistant To Negative And Positive Water Pressure PRODUCT DESCRIPTION Cement based single component waterproofing mortar, which is resistant to positive and negative water pressure and which penetrates into capillary gaps for waterproofing purposes. AREAS OF USE Megaİzo Kristalize is used for negative and positive waterproofing of sound concrete surfaces in independent swimming pools, sewage and waste water treatment plants, basements, water tanks, elevator shafts, warehouses and parking garages. It is suitable for use on horizontal and vertical surfaces of indoors and outdoors spaces. PRODUCT ADVANTAGES • Fit for contact with drinking water. • Provides the surface with resistance to both negative and positive water pressure. • Easily settles into capillary cracks, fills such cracks, forming a crystal structure, and so ensures waterproofing. PERFORMANCE TYPE: CM, waterproofing material with cement content, applied in liquid form, which, under standard conditions, poses crack bridging capability under standard conditions and at low temperatures. Initial adhesion strength ≥ 0.5 N/mm 2 TS EN 14891 : 2012 Adhesion strength after water contact ≥ 0.5 N/mm 2 TS EN 14891 : 2012 Adhesion strength after thermal ageing ≥ 0.5 N/mm 2 TS EN 14891 : 2012 Adhesion strength after freezing – thawing cycles ≥ 0.5 N/mm 2 TS EN 14891 : 2012 Adhesion strength after hard water contact ≥ 0.5 N/mm 2 TS EN 14891 : 2012 Waterproofing No penetration, ≤ 20 gr increase in mass (≥ 5 bars) TS EN 14891 : 2012 (positive; negative) Crack bridging capability under standard conditions ≥ 0.75 mm TS EN 14891 : 2012 The foregoing values represent the results of the laboratory tests conducted at 23 ± 2°C temperature and 50% ± 5 relative humidity conditions. The values provided as per the table may vary depending on the surface and ambient conditions. REFERENCE STANDARDS Certifications/Standards TS EN 1504 - 2 Ministry of Public Works and Settlement Item No. Ministry of Public Works and Settlement Item No.: 04.477/2 QUALITY CERTIFICATES Certificate for suitability for contact with drinking water issued by Water Quality Center, UK according to BS 6920: 2000 (Report Reference No: M 105590) - (24.01.2014) Conformant to TS EN 1504 - 2. CE APPLICATION PROCEDURE Application Surfaces Indoors and Outdoors Walls; - Cement based plaster - Concrete Indoors and Outdoors Floors; - Cement based trowel coating - Concrete Surface Preparation • The application surface should be dry, clean, sound and dust-free, and should have been cleansed of oil, dirt or any materials that may prevent adhesion, and any such materials as mortar and cement residues should be scraped from the application surface. • Such surfaces as concrete and cement based plaster should be moisturized carefully with clean water immediately before the application. The application should be started after the drainage of the surface water and due care must be taken to make sure that the application surface is moist, not wet. Application Methods • Megaİzo Kristalize is applied on the moisturized surface with a brush, which should be over saturated with water, in double coat. Once the primary coat thoroughly dries, the secondary coat should be applied as perpendicularly to the primary coat. • Following the application, the product should be moisturized for 5 days in order for the product to penetrate into the surface. • In the cases, where a subsequent coat application is to be performed 12 hours later or after a longer period of time, the surface should moisturized again prior to application. Application Recommendations • The surface should, subsequently to Megaİzo Kristalize application, be protected from external weather conditions and thermal impacts with a plastic cover. • The material applied should be moisturized and protected from exposure to direct sunlight and such factors as frost for 5 days following the application. • Megaİzo Kristalize should, once prepared, be used before the expiration of its pot life. Any product, the pot life of which has expired, should not be used during the application. • Any such foreign substance as lime, cement or plaster should not be added to the mortar prepared. • Any extra water should not be added to the mixture. • The product should not be applied on unsound surfaces. The soundness and the load bearing capacity of old surfaces should be checked prior to adhesion. • The surface should be protected from air currents during and after the application. • The product should not be applied to such surfaces, which are exposed to risk of freezing within the next 24 hours, which are frozen or the frost of which is thawing. • Due care should be taken to ensure that the material is not exposed to direct sunlight in hot weather conditions, and the product should be mixed with cold water. • The product should not be applied on extremely windy weather conditions or on hot surfaces, which are exposed to direct sunlight; and in the cases, where application is imperative under such conditions, the environment and the surface should be prepared for application in advance. • The product should not be applied in rainy weather conditions, and the application surface should be preserved from rain for a period of 24 hours. • Refer to our technical support hotline for recommendation on different surface applications. (PHONE: 444 4 595) Surface and Ambient Temperature The surface and ambient temperature should be between +5°C and +30°C whilst at application. Application Limits Useful time for prepared mortar - Pot life Required standby time before the application of subsequent coat Required standby time before subsequent application The foregoing values represent the results of the laboratory tests conducted at 23 ± 2°C temperature and 50% ± 5 relative humidity conditions. The values provided as per the table may vary depending on the surface and ambient conditions. APPLICATION INSTRUCTIONS Mixing Ratio The product should be mixed with water, weighing equal to 30 - 32 % of the product. (7.5 - 8.0 liters of water for a 25 kg package) Mixing Equipment • Low speed electrical mixer (400 cycles/min.) Mixing Period The product should be stirred with a low-speed mixer until any dry dust and globs are eliminated. The mortar should, then, be stirred once again for 1 to 2 minutes after being had settled for 3 to 4 minutes following preparation. Application Equipment • Brush Maximum 30 minutes Minimum 6 hours Minimum 7 days Equipment Cleaning The equipment used should be cleaned with water following the application before the mortar dries. TECHNICAL PROPERTIES Chemical Structure: Cement based waterproofing mortar, containing water repellant additives Dry Density: 1.50 ± 0.01 gr/cm 3 Mortar Density: 1.75 ± 0.01 gr/cm 3 Grain Size: ≤ 600 µm Color: Gray CONSUMPTION Recommended consumption amount for double coat application (in roughly 2 mm thickness) on 1 m 2 surface is 3.0 - 3.2 kg. The said values may vary, depending on the surface and ambient conditions. 67
PACKAGING Megaİzo Kristalize is delivered in net 25 kg kraft bags, which are stowed in 54 pcs. on a 80 cm x 100 cm palette (1350 kg). SHELF LIFE The shelf life of the product is 12 months when stored within non-tampered original packaging in dry (maximum relative humidity 60 %) and cool (ambient temperature between +5°C and +25°C) environment. STORAGE CONDITIONS The product should be stored within non-tampered original packaging in dry (maximum relative humidity 60 %) and cool (ambient temperature between +5°C and +25°C) environment. It should not be exposed to direct sunlight. The container of the product should be closed firmly when not used. SAFETY PRECAUTIONS Please refer to the Safety Data Sheet (SDS) as appropriate for easy and safe application. 68
- Page 1 and 2:
ADHESIVES MegaFix MegaFix K MegaGra
- Page 3 and 4:
Equipment Cleaning The equipment us
- Page 5 and 6:
Mortar Density: 1.85 ± 0.05 gr/cm
- Page 7 and 8:
CONSUMPTION The consumption amount
- Page 9 and 10:
Application Equipment • Steel not
- Page 11 and 12:
Equipment Cleaning The equipment us
- Page 13 and 14: Application Equipment • Steel not
- Page 15 and 16: Grain Size: ≤ 600 µm Color: Gray
- Page 17 and 18: Equipment Cleaning The equipment us
- Page 19 and 20: Application Equipment • Steel not
- Page 21 and 22: Equipment Cleaning The equipment us
- Page 23 and 24: Temperature Resistance: -15°C to +
- Page 25 and 26: MegaPro Pastemix Polymer Emulsion B
- Page 27 and 28: MegaEpoxy Epoxy Resin Based, Double
- Page 29 and 30: MegaBlok Cement Based, Gas Concrete
- Page 31 and 32: ARTEFIX Cement Based Ceramic Adhesi
- Page 33 and 34: BRUFIX Cement Based Ceramic Adhesiv
- Page 35: JOINT FILLERS MegaFuga MegaFuga Sil
- Page 38 and 39: Consumption Amount Calculation Meth
- Page 40 and 41: CONSUMPTION The consumption amount
- Page 42 and 43: CONSUMPTION The consumption amount
- Page 44 and 45: Consumption Amount Calculation Meth
- Page 46 and 47: RECOMMENDED MegaFuga Rustik CONSUMP
- Page 48: Application Limits Useful time for
- Page 51 and 52: Megaİzo Lastik Mono Cement Based,
- Page 53 and 54: Megaİzo Lastik 7 Polymer Emulsion
- Page 55 and 56: Megaİzo Lastik 10 Polymer Emulsion
- Page 57 and 58: Megaİzo Lastik 15 Polymer Emulsion
- Page 59 and 60: Megaİzo Lastik 3 Hydrophobic Impre
- Page 61 and 62: PACKAGING Megaİzo Lastik 5 is deli
- Page 63: CONSUMPTION Recommended consumption
- Page 67 and 68: TECHNICAL PROPERTIES Chemical Struc
- Page 69 and 70: Equipment Cleaning The equipment us
- Page 71 and 72: Megaİzo PK3/PK4 - PK3/PK4 Plus - P
- Page 73 and 74: Megaİzo PU 7 Polyurethane Based, R
- Page 75 and 76: Megaİzo PU 10 Polyurethane Based,
- Page 77 and 78: Megaİzo PU 15 Polyurethane Based,
- Page 79 and 80: Megaİzo PU 6 Bitumen Modified, Dou
- Page 81 and 82: Megaİzo PU Mastik LM Polyurethane
- Page 83 and 84: Megaİzo PU Mastik HM Polyurethane
- Page 85 and 86: Megaİzo Stoper Cement Based, Insta
- Page 87 and 88: Megaİzo File Reinforcement And Gla
- Page 90 and 91: REPAIR MORTARS MegaTamir İ MegaTam
- Page 92 and 93: MegaTamir K Cement Based Repair And
- Page 94 and 95: MegaTamir K Yapısal Cement Based S
- Page 96 and 97: MegaTamir Epo Epoxy Based Adhesive
- Page 98 and 99: MegaTamir EpoGrout Epoxy Based, Thr
- Page 101 and 102: FLOORING MATERIALS MegaZemin SL20 M
- Page 103 and 104: MegaZemin BYS Surface Hardening Mor
- Page 106 and 107: PLASTERS MegaSıva İ MegaSıva K M
- Page 108 and 109: PACKAGING MegaSıva İ is delivered
- Page 110 and 111: - Gas concrete surface: 17.5 - 18.5
- Page 112 and 113: PACKAGING MegaSıva Saten is delive
- Page 114 and 115:
PACKAGING MegaSıva Perlitli is del
- Page 116 and 117:
- Gas concrete surface: 1.5 - 2.5 k
- Page 118 and 119:
CONSUMPTION Recommended consumption
- Page 120 and 121:
PACKAGING MegaSıva Makine İç is
- Page 122 and 123:
PACKAGING MegaSıva Makine Dıº is
- Page 124:
MegaSıva Thermo Plaster Mortar For
- Page 127 and 128:
MegaFilm Multipurpose Surface Prepa
- Page 129 and 130:
MegaFilm Visko Environmental Friend
- Page 131 and 132:
MegaFilm İzo Bitumen Emulsion Base
- Page 133 and 134:
MegaFilm İzo Epo Epoxy Based, Doub
- Page 136 and 137:
ADDITIVES & AUXILIARY MATERIALS Meg
- Page 138 and 139:
MegaAntiFreeze 10 Anti-Freeze Morta
- Page 140 and 141:
MegaClean Ready To Use Joint And Su
- Page 142 and 143:
Mantotherm Adhesive Mortar Adhesive
- Page 144 and 145:
Mantotherm Primer Acrylic Emulsion
- Page 146 and 147:
Mantotherm Dekominera - Lined Textu
- Page 148 and 149:
Mantotherm Exterior Paint With Sili
- Page 150 and 151:
Mantotherm Grained Exterior Coating
- Page 152 and 153:
Mantotherm EPS Thermal Insulation P
- Page 154 and 155:
Mantotherm XPS Thermal Insulation P
- Page 156 and 157:
Mantotherm Glass-Fiber Mesh Glass-F
- Page 158 and 159:
151
- Page 161 and 162:
k k k k k k k k k
- Page 163 and 164:
k k k k k k k k k k k k k k
- Page 165 and 166:
k k k k k k k
- Page 167 and 168:
Areas Of Use
- Page 169 and 170:
Areas Of Use
- Page 171 and 172:
Areas Of Use
- Page 173:
Areas Of Use