Table 4.08 TATB (PURIFIED)
Composition
100 wt%
Theoretical
TATB
_ --
Maximum Density
1.938 g/cm3
Particle Size Distribution
Wt%: below 10 pm = 4.51; below 25 pm = 41.10; below 30 pm
= 53.3; below 45 pm = 77.8.
Surface area over range = 22.62 cm’/g.
Preparation Method
Pressing, and machining to shape
Data Summary
Technique 4
Coordinates
High-Order
for
Initial Shock Parameters Detonation
Shot T, P, UP0 U.0 l/2 b X* t*
Number (“C) (GPa) (mm/ps) (mm/Fs) (mm/d (mm) (/Js)
___--~ ~ ~
p. = 1.876 g/cm3
E-3646 -23 0.57 0.152 1.999 -0.0126 >>12.72 B5.80
0.67 0.179
E-3672 -23 2.89 0.489 3.151 0.0503 >>12.47 >>3.77
E-3587 -23 3.02 0.480 3.356 0.0113 >>12.71 >>3.69
E-3569 -23 6.74 0.858 4.186 0.049 B12.65 >>2.92
E-3568 -23 9.42 1.063 4.723 0.111 >12.74 >2.44
E-3558 -23 11.40 1.208 5.030 0.319 7.66 1.38
w
G
E-3549
E-3559
-23
-23
13.03
16.22
1.340
1.471
5.184
5.879
0.425
0.684
5.80
3.23
1.02
0.52
Driving
System Thickness
(mm)
A, 11.4 SS, 10.9 Plex
B, 17.8 polyethylene,
11.4 SS, 10.9 Acrylite
B, 17.8 polyethylene,
11.4 SS, 9.7 Acrylite
B, 48.5 Plex
G, 38.1 Plex
G, 18.0 Acrylite
G, 12.2 Everkleer
G, 6.4 Plex