SHOCK INITIATION PROPERTIES
422
Table 4.51 VRP CLASS VII PROPELLANT
Preparation Method
Vacuum casting, pressure curing, and machining to shape
Data Summary
p. = 1.836 g/cm3. To = 24°C. Technique 7
Coordinates for
High-Order
Initial Shock Parameters Detonation Driving
Shot P@ UDO u., x* t* System Thicknness
Number (GPa) (rn&‘ks) (mm/ps) (mm) (PS) (mm)
--
E-4513 3.42 0.548 3.40 >25.5 >7.15
E-4514 5.27 0.718 4.0 8.55 2.17
E-4524 3.65 0.542 3.67 22.6 5.81
E-4526 6.27 0.835 4.09 5.69 1.28
E-4533 5.42 0.738 4.00 9.40 2.21
E-4534 4.35 0.653 3.63 21.1 5.48
E-4541 6.26 0.784 4.35 5.75 1.27
E-4545 7.20 0.872 4.5 5.21 1.03
Reduced Data
U,, = (1.992 f 0.365) + (2.761 f 0.507)U,,.
Table 4.52 VTG-5A CLASS VII PROPELLANT
Preparation Method
Vacuum casting and pressure curing
Data Summary
p,, = 1.839 g/cm3. T, = 24°C. Technique 7
Coordinates for
High-Order
Initial Shock Parameters Detonation
Shot x* t*
Number (G?a) (rn2Ms) (m$Fs) (mm) (ps)
--
E-4506 6.01 0.760 4.3 7.08 1.82
E-4515 5.52 0.728 4.12 7.53 1.76
E-4516 5.79 0.749 4.20 7.64 1.80
E-4518 3.53 0.545 3.52 >25.5 >6.79
E-4532 3.68 0.572 3.50 23.0 6.05
E-4537 7.25 0.876 4.5 4.68 0.97
E-4546 4.45 0.637 3.80 14.9 3.70
Reduced Data
u,, = (1.703 f 0.177) + (3.292 f 0.251)U,,.
B, 24.1 SS, 23.3 PMMA
H, 19 SS, 19.0 PMMA
B, 24.1 SS, 14.8 PMMA
K, 24.1 SS, 10.9 PMMA
G, 19 SS, 10.9 PMMA
B, 19 SS, 10.9 PMMA
K, 24.1 SS, 10.9 PMMA
L, 24.1 SS, 10.9 PMMA
Driving System Thickness
(mm)
H, 24.1 SS, 10.9 PMMA
H, 19.0 SS, 10.9 PMMA
L, 24.1 SS, 23.7 PMMA
C-l, 24.1 SS, 23.7 PMMA
B, 19 SS, 10.9 PMMA
L, 24.1 SS, 10.9 PMMA
D, 19.0 SS, 10.9 PMMA