SHOCK INITIATION PROPERTIES
402
Table 4.34 94 TATB (BIMODAL)/G ESTANE
Composition
94 wt% TATB (bimodal), 6 wt% Estane
Theoretical Maximum Density
1.869 g/cm3
Particle Size Distribution
Bimodal
Preparation Method
Hot pressing and machining to shape
Data Summary
p. = 1.833 g/cm3. T,, w 23°C. Technique 3
Coordinates for
High-Order
Initial Shock Parameters Detonation Driving
Shot P, UP0 UIO X* t* System Thickness
Number (GPa) (mm/Bs) (mm/ps) (mm) Gs) (mm)
- -
E-2915 12.00 1.299 5.040 17.14 3.04 G, 12.2 PMMA
E-2889 13.40 1.350 5.414 10.16 1.70 H, 11.9 Plex
E-2913 17.82 1.677 5.796 5.25 0.84 J, 12.1 PMMA
E-2890 25.72 2.139 6.560 1.46 0.21 N, 6.1 Plex
Reduced Data
U,, = (3.032 f 0.358) -t (1,652 f 0.217)U,,.
log P = (1.47 f 0.02) - (0.32 f 0.02) log x*.
log P = (1.21 f 0.81) - (0.29 f 0.02) log t*.