SHOCK INITIATION PROPERTIES
404
Table 4.36 94 TATB/4.5 PS/1.5 DOP
Composition
94 wt% TATB, 4.5 wt% polystyrene, 1.5 wt% dioctylphthalate (DOP)
Theoretical Maximum Density
1.841 g/cm3
Particle Size Distribution
Standard
Preparation Method
Hot pressing and machining to shape
Data Summary
To = 23°C. Technique 3
Coordinates
High-Order
for
Initial Shock Parameters Detonation
Driving
Shot
Number
P,
(GPa)
UPI
(mm/MS)
US,
(mm/MS)
X*
-
(mm)
t*
- (YS)
System Thickness
(-)
p. = 1.817 g/cm3
E-2906 12.88 1.403 5.054 16.84 2.97 F, 12.3 Plex
E-2851 15.24 1.523 5.508 9.06 1.49 H, 6.2 Plex
E-2914 17.40 1.674 5.719 7.22 1.15 J, 12.1 PMMA
E-2887 25.62 2.083 6.768 1.60 0.22 N, 6.0 Plex
p. = 1.825 g/cm3
E-2903 15.32 1.526 5.498 14.43 2.45 H, 12.2 Plex
E-2850 17.01 1.642 5.675 10.72 1.77 H, 6.1 Plex
E-2888 25.86 2.080 6.813 1.78 0.23 N, 6.0 Plex
Reduced Data
U,, = (1.69 f 0.185) + (2.448 f O.l07)U,,.
log P = (1.47 f 0.03) - (0.27 f 0.03) log x”.
log P = (1.25 f 0.01) - (0.24 f 0.02) log t*.