Values<br />
TECAST T<br />
TECARIM<br />
(PA 6 C) (PA 6 C)<br />
T g 40 °C 53 °C<br />
Density 1.15 g/cm 3 1.11 g/cm 3<br />
Modulus of elasticity 3,500 MPa 2,200 MPa<br />
Service temperature, long-term 100 °C 95 °C<br />
Service temperature, short-term 170 °C 160 °C<br />
Lower service temperature -40 °C -50 °C<br />
Identifying characteristics<br />
ˌˌColour opaque / milky white<br />
ˌˌHigh flammability<br />
ˌˌBurns with a blue flame with yellow tip,<br />
no or only minimal sooting<br />
ˌˌHorn-like odour when burning,<br />
produces melted droplets, draws threads<br />
ˌˌDensity slightly above 1 g/cm³,<br />
floats in saturated salt solution<br />
ˌˌTranslucent with thin wall thicknesses / at the edges<br />
Products / Modifications<br />
TECAST T (PA 6 C)<br />
Basic type, tough-hard,<br />
very good machining properties<br />
TECAGLIDE green<br />
(PA 6 C, solid lubricant)<br />
Cast PA 6, sliding properties<br />
modified for very low friction<br />
TECAST L (PA 6 C, oil)<br />
Sliding properties modified<br />
TECAST L black (PA 6 C, oil)<br />
Sliding properties modified,<br />
black, also for outdoor exposure<br />
to weather<br />
TECAST L yellow (PA 6 C, oil)<br />
Sliding properties modified, yellow<br />
TECAST TM (PA 6 C, MoS 2 )<br />
With MoS 2 , improved abrasion<br />
resistance, suitable for outdoor<br />
exposure to UV<br />
TECARIM 1500 yellow<br />
(PA 6 C, elastomer)<br />
Signal colour yellow,<br />
high toughness, good low<br />
temperature impact strength<br />
Application examples<br />
Pulleys and guide rollers, chain guides, slide rails. <strong>The</strong> adjustable<br />
toughness properties of TECAST T are used in<br />
damping plates for impact and vibration hammers applied<br />
for pile driving; large-scale gears used for the transfer of<br />
motion rather than power transmission.<br />
Due to its high toughness, TECARIM is also used at low<br />
temperatures for winter technology applications (chain supports,<br />
chain buffers for bulldozers); Stress relief blocks for<br />
punching, deep drawing in automotive production, white<br />
goods, tool building<br />
Summary<br />
Due to its relatively high but reversible moisture absorption,<br />
PA 6 has a high level of toughness, whereby TECAST<br />
T demonstrates even higher crystallinity and better machinability<br />
than PA 6.<br />
TECAST L and TECAGLIDE are special types with modified<br />
sliding properties for improved sliding friction properties<br />
and reduced abrasion.<br />
Several TECARIM types can be varied over wide ranges (in<br />
terms of strength, creep strength and toughness from<br />
tough elastic to hard).<br />
23