a) b - École Polytechnique de Montréal

More documents

Recommendations

Info

Continuity (%) of PS phase a) 100 90 80 70 60 50 40 30 20 10 0 a b 0 10 20 30 40 50 60 70 80 90 100 Volume fraction of HDPE(HDPE%+PS% = 60% of total) c b) c) d) e) f) Figure 6-11. PS continuity and the corresponding morphology as a function of HDPE concentration following Scheme (a) from Figure 6-10. The PMMA phase concentration is held constant at 40% volume fraction in all samples. In the schematics, green is the PMMA phase, red is the PS phase and blue is the HDPE phase. d e f 196
Addition of a low concentration of HDPE to the system leads to the encapsulation of HDPE droplets in a highly continuous PS network resulting in a bi-continuous/dispersed phase morphology and a slight reduction of PS continuity(point b in Figure 6-11). A further increase of HDPE phase generates a tri-continuous morphology(type II) where the coalescence of HDPE droplets forms a continuous phase of HDPE in highly continuous PS (point c in Figure 6-11). Note that at point c for the 30/30/40 HDPE/PS/PMMA blend, the continuity level of PS is lowered to 68% Such a <strong>de</strong>crease in the continuity level is attributed to the entrapment of some parts of the PS phase in the PMMA network. Point d indicates the expected drop in continuity after the formation of the type I tricontinuous structure at point e. At point e, the 82% HDPE volume fraction corresponds to the 50/10/40 HDPE/PS/PMMA blend. This type I tri-continuous structure with a PS continuity of 76% represents the case where 50% HDPE and 40% PMMA form a co-continuous structure with a thin PS layer situated at the HDPE/PMMA interface. Finally, replacing all the PS with HDPE results in a (60%HDPE matrix/40%PMMA dispersed phase) blend (point f in Figure 6-11). Local maximum continuity of 78% is obtained for 48/12/40 HDPE/PS/PMMA blend from Figure 6-11. The most important observation for scheme a, where the PMMA concentration is held at 40%, is that due to the thermodynamic limitations of spreading, the system is never able to form PS droplets even at a very low concentration of PS. PS always spreads between HDPE and PMMA in or<strong>de</strong>r to separate those two components. Thus even the smallest amount of PS in scheme a) presents a layer structure as opposed to droplets. In scheme (b), from Figure 6-10, the concentration of the PS phase is kept constant at 10% volume fraction and the concentration ratio of the two other phases changes. In Figure 6-12, the continuity of the PS phase following Scheme b is examined as a function of the % concentration of HDPE in (HDPE plus PMMA) where HDPE plus PMMA always equals 90% in the ternary blend with PMMA. Thus, 100% HDPE refers to the 90%HDPE/10%PS blend, while 50% HDPE in Figure 6-12 refers to the 45%HDPE/10%PS/45%PMMA blend. This scheme allows for the study of the effect of the composition of the inner phase(HDPE) and the outer phase(PMMA) on the morphology of the middle phase(PS). It is interesting to note that in this case, the PS continuity curve is almost symmetric. At 0% HDPE, the continuity of PS is zero due to the presence of PS droplets within the matrix of PMMA(point a in Figure 6-12). 197
Page 1 and 2:
© Sepehr Ravati, 2010. UNIVERSITÉ
Page 3 and 4:
DEDICATED To my parents iii
Page 5 and 6:
RÉSUMÉ Cette thèse présente, po
Page 7 and 8:
devenir une structure hiérarchique
Page 9 and 10:
ABSTRACT This thesis presents, for
Page 11 and 12:
system can be increased from 10 -15
Page 13 and 14:
CONDENSÉ EN FRANÇAIS Dans ce trav
Page 15 and 16:
deuxième coquille de PS. Les phase
Page 17 and 18:
structures à percolation multiple
Page 19 and 20:
autre sous-type de morphologie dans
Page 21 and 22:
TABLE OF CONTENTS DEDICATION.......
Page 23 and 24:
xxiii 2.4.1.1.1 Charged Polymer Ads
Page 25 and 26:
5.3.4 Annealing Test ..............
Page 27 and 28:
xxvii REFERENCES ..................
Page 29 and 30:
LIST OF FIGURES xxix Figure 1-1. a)
Page 31 and 32:
Figure 2-12. SEM photomicrograph of
Page 33 and 34:
Figure 2-34. Schematic view of diff
Page 35 and 36:
Figure 4-8. SEM micrographs of vari
Page 37 and 38:
Figure 5-6. a),b) Scanning electron
Page 39 and 40:
and c) triangular concentration dia
Page 41 and 42:
n number of moles p concentration o
Page 43 and 44:
AFM atomic force microscopy LIST OF
Page 45 and 46:
PS-co-PMMA copolymer of PS and PMMA
Page 47 and 48:
1.1 Introduction CHAPTER 1 - INTROD
Page 49 and 50:
Figure 1-2. Human heart, longitudin
Page 51 and 52:
One of the applications for porous
Page 53 and 54:
On the other hand, a novel tri-cont
Page 55 and 56:
2.1 Polymer Blends CHAPTER 2 - LITE
Page 57 and 58:
Based on Sterling’s approximation
Page 59 and 60:
Antonoff’s rule (Equation 2-13) i
Page 61 and 62:
2.1.2.1 Binary Polymer Blends 2.1.2
Page 63 and 64:
Some other studies(Everaert, Aerts,
Page 65 and 66:
where the parameter z is dependent
Page 67 and 68:
“compatibilization” was suggest
Page 69 and 70:
a) λ BC A and B are matrices, b) C
Page 71 and 72:
Reignier & Favis, 2000, 2003a; Reig
Page 73 and 74:
measure the interfacial tension of
Page 75 and 76:
a) b) Figure 2-6. Dependence of the
Page 77 and 78:
Omonov et al. found double percolat
Page 79 and 80:
2.1.2.2.3 Effect of Composition on
Page 81 and 82:
a) b) C B A c) Figure 2-12. SEM pho
Page 83 and 84:
In the case where PS is the matrix,
Page 85 and 86:
Posthuma de Boer, 1999) (Kumin & Ch
Page 87 and 88:
lattice, such as square lattice, wi
Page 89 and 90:
magnetization, which is a function
Page 91 and 92:
Polymers have long been thought of
Page 93 and 94:
epoxy as a function of nanotube wei
Page 95 and 96:
Figure 2-19. Approaching the percol
Page 97 and 98:
Figure 2-21. Transmission electron
Page 99 and 100:
Figure 2-22: Dependence of PE conti
Page 101 and 102:
Figure 2-24. Plot of the total numb
Page 103 and 104:
chain provides the conductive path
Page 105 and 106:
2.3.1.2.1 Polyaniline One of the mo
Page 107 and 108:
CoPA/LLDPE/PANI blend and a poor-qu
Page 109 and 110:
Narkis and co-workers extended and
Page 111 and 112:
Figure 2-31: Conductivity of PVDF/P
Page 113 and 114:
organic thin films, a novel and str
Page 115 and 116:
on the topic have been reported in
Page 117 and 118:
succeeded in creating thin films wi
Page 119 and 120:
Addition of salt to the solution of
Page 121 and 122:
different from that of linear homop
Page 123 and 124:
Figure 2-39. Macromolecule with a)
Page 125 and 126:
polyanion such as hyaluronan (HA)(P
Page 127 and 128:
2.4.1.1.7 Effect of Salt on Multila
Page 129 and 130:
2.4.1.1.8 Overcompensation of the M
Page 131 and 132:
important factors determining the g
Page 133 and 134:
As shown in Figure 2-44, swelling a
Page 135 and 136:
increasing the pH value due to a de
Page 137 and 138:
CHAPTER 3 - ORGANIZATION OF THE ART
Page 139 and 140:
discussed above, HDPE, PS, PMMA, an
Page 141 and 142:
CHAPTER 4 - LOW PERCOLATION THRESHO
Page 143 and 144:
or model which predicts where the p
Page 145 and 146:
concentration threshold for the ons
Page 147 and 148:
chemical and weathering resistance,
Page 149 and 150:
Table 4-1. Material Characteristics
Page 151 and 152:
filled with blend pellets. To facil
Page 153 and 154:
4.3.6 Conductivity Measurements DC
Page 155 and 156:
experimentally in this research gro
Page 157 and 158:
a) b) c) d) Figure 4-4. Schematic i
Page 159 and 160:
microstructure of the quaternary bl
Page 161 and 162:
a) b) c) d) Figure 4-6. SEM microgr
Page 163 and 164:
a) b) PVDF PS PMMA c) d) e) HDPE PS
Page 165 and 166:
Uniform layers of PS and PMMA situa
Page 167 and 168:
the concentration of HDPE is increa
Page 169 and 170:
a) b) c) e) Figure 4-11. SEM microg
Page 171 and 172:
melt-processable and contains 25 wt
Page 173 and 174:
One question that should be address
Page 175 and 176:
Conductivity(S/cm) Ternary Blend 1,
Page 177 and 178:
phase(PMMA), the concentration of P
Page 179 and 180:
(6) Virgilio, N.; Desjardins, P.; L
Page 181 and 182:
ONION MORPHOLOGY HDPE PVDF PS Contr
Page 183 and 184:
work described above has focused on
Page 185 and 186:
thermodynamic explanation to predic
Page 187 and 188:
four-point probe increases continuo
Page 189 and 190:
in the rheology tests were compress
Page 191 and 192: 5.3.6 Layer-by-Layer Deposition The
Page 193 and 194: prepare a polymer blend structure w
Page 195 and 196: a) b) c) Figure 5-3. Scanning elect
Page 197 and 198: spontaneously self-assembled. After
Page 199 and 200: a) b) c) d) e) f) g) h) Figure 5-5.
Page 201 and 202: Since the ultra-low surface area va
Page 203 and 204: c) a) b) Figure 5-6. a),b) Scanning
Page 205 and 206: salt to a PSS polyelectrolyte solut
Page 207 and 208: A relationship between macropore si
Page 209 and 210: close together. It is interesting t
Page 211 and 212: Figure 5-9. Mass increase (%) indic
Page 213 and 214: In this work the conductance of the
Page 215 and 216: deposited PANI layers increases unt
Page 217 and 218: (52) Guo, H. F.; Packirisamy, S.; G
Page 219 and 220: 6.2 Introduction It is well-known t
Page 221 and 222: modified version of Harkins theory(
Page 223 and 224: 6.3 Experimental 6.3.1 Materials Co
Page 225 and 226: Complex voscosity (Pa.s) 1,0E+04 1,
Page 227 and 228: 6.3.5.2 Focused Ion Beam (FIB) and
Page 229 and 230: a) c) b) d) e) f) PMMA PMMA HDPE HD
Page 231 and 232: y Harkins theory, PS will always si
Page 233 and 234: a) b) c) d) e) f) PS Figure 6-6. a)
Page 235 and 236: a) b) HDPE : black PS : grey PMMA :
Page 237 and 238: 6.4.6 Continuity, Co-continuity, an
Page 239 and 240: c) V III II I VII I IV VI Figure 6-
Page 241: Continuity Scheme (a) Figure 6-10.
Page 245 and 246: Addition of small amounts of HDPE t
Page 247 and 248: icontinuous network with the HDPE.
Page 249 and 250: Three examples are shown in Figure
Page 251 and 252: (9) Mekhilef, N.; Verhoogt, H. Poly
Page 253 and 254: structures are formed due to the co
Page 255 and 256: CONCLUSION AND RECOMMENDATIONS In t
Page 257 and 258: REFERENCES A. K. Gupta, K. R. S. (1
Page 259 and 260: Caruso, F. (2003). Hollow Inorganic
Page 261 and 262: Domenech, S. C., Bortoluzzi, J. H.,
Page 263 and 264: Geuskens, G., Gielens, J. L., Geshe
Page 265 and 266: Hou, S., Harrell, C. C., Trofin, L.
Page 267 and 268: Krass, H., Papastavrou, G., & Kurth
Page 269 and 270: Macdiarmid, A. G., Jin-Chih, C., Ha
Page 271 and 272: Niziol, J., & Laska, J. (1999). Con
Page 273 and 274: Reghu, M., Yoon, C. O., Yang, C. Y.
Page 275 and 276: Shirakawa, H., Louis, E. L., MacDia
Page 277 and 278: Utracki, L. A. (1991). On the visco
Page 279 and 280: Yasuda, K., Armstrong, R., & Cohen,
Page 281 and 282: literature has examined factors inf
Page 283 and 284: (Reignier & Favis, 2000, 2003a; Rei
Page 285 and 286: Table A-1.2. Interfacial tensions a
Page 287 and 288: acquisition of images with a very h
Page 289 and 290: Table A-1.3. Continuity of the PMMA
Page 291 and 292: (17) Reignier, J.; Favis, B. D., Ma
Page 293 and 294:
PANI. Theoretically, the extent of
Page 295 and 296:
Equation A-2.7 0( ) 0 1. 5 σ = σ
Page 297 and 298:
Cumulative Mass × 10 5 (g) dipping
Page 299 and 300:
of PANI, and an increase in the con
Page 301 and 302:
Resistance(ohm) 1.0E+12 1.0E+11 1.0
Page 303 and 304:
esistance value. Samples containing
Page 305 and 306:
The results of resistance for PS/PE
Page 307 and 308:
Caruso, F., & Schuler, C. (2000). E
show all

a) b - École Polytechnique de Montréal