02 - BTI - We know your business

1006
* Definitions in accordance with DIN 52452, part 4
Coating compat bility:
On an already existing surface coating a sealing
compound is used (test A1)
�����
Technical data for sealing compounds/sealing masses
SI-N sealing compound
Sealing compound
Natural stone
silicone
Sealing compound
SI-A
A surface coating is applied to a fully cured sealing
compound in the adjoining area (test A2)
Sealing compound
Sanitary
Sealing compound
High temperature
silicone
Crude material base Silicone Silicone Silicone Silicone Silicone
Hardening system Humidity curing
Outside wall joints
acc. to DIN 18540
Glazing
acc. to DIN 18545
•
Sealing compound
MS-P
MS
polymer
•
Sealing compound
Diskit/ Structure
diskit (diskittransparent)
Dispersion
acrylate
Water
evaporation
Coatability:
The entire surface of the sealing compound is coated
(test A3)
Note:
Based on our current state of knowledge there are no
coating systems for windows and facades yet which
resist 20 or 25% strain or compression without cracking.
No sealing compound of groups C, D or E can thus
be deemed overcoatable.
The details specified in this publication are based on our current knowledge and experience. Due to the abundance of possible processing and application influences this information does not release the processor from performing his
own tests and trials. Legally binding assurance of certain characteristics or suitability for a concrete implementation objective can not be derived from this information.
Sealing compound
Supraflex roof
Synthetic
rubber
Solvent
evaporation
Film adhesive
Acrylic acid
ester
dispersion
Water
evaporation
Sealing compound
Acrylos
Sealing compound
Bitumplast
Acrylate
dispersion Bitumen
Solvent evaporation
Overcoatable* • • • • •
Coating compatible* • • • • • • • • • • •
Fungicide equipped
(antifungal)
1* • • • •
Adhesion on humid
• • • •
surfaces
Bitumen compatible • •
Silicone-free • • •
Technical data
Max. permitted permanent
movement absorption
approx.
25 % 25 % 25 % 20 % 25 % 25 % 12.5 %
(10 %)
Sealing compound
Fire kit
Sodium
silicate
Ventilation duct
sealing compound
Polyacrylate
Water
evaporation
25 % 10 % 5 % 5 % nz 20 %
Reduction approx. 5 % 0 % 4 % 4 % 5 % 0 % 15 %
(37 %)
20 % – 19 % 0 % 0 % 15 %
Minimum joint width 5 5 5 5 2 5 nz 5 nz 5 nz nz nz
Maximum joint width 30 30 30 30 25 30 25 10 nz 10 nz nz nz
Skin building time
in minutes approx.
10– 15 10 – 15 10 – 15 10 – 15 15 10 5 – 10 15 – 20 nz 5 5 nz 10
Through hardening speed 2 mm/ 2 mm/ 2 mm/ 2 mm/ 1.5 mm/ 2 mm/ 3 mm/ 2 – 3 mm/ 2 – 3 days 2 mm/ 3 mm/ 1 – 2 mm/ 1.5 mm/
approx.
24 hrs 24 hrs 24 hrs 24 hrs 24 hrs 24 hrs Week 24 hrs
week Week 24 hrs day
Non-adhesiveness of sur- 2 – 3 2 – 3 2 – 3 2 – 3 1 2 – 3 2 – 3 2 – 3 nz Approx. 24 nz 2 – 3
face within hours
24 - 48
Temperature resistance -50/ -60/ -50/ -20/ -60/ -40/ -20/ -25/ -30/ -20/ -20/ -20/ -20/
in °C
+150 °C +180 °C +150 °C +150 °C +260 °C +90 °C +75 °C +100 °C +120 °C +70 °C +70 °C +1,500 °C +80 °C
Processing temperature +1/ +1/ +1/ +1/ +5/ +1/ +5/ +5/ +5/ +5/ +5/ +5/ +5/
in °C
+30 °C +30 °C +30 °C +30 °C +40 °C +30 °C +30 °C +40 °C +40 °C +30 °C +30 °C +30 °C +50 °C
Suitable smoothing agent:
BTI smoothing agent
• • • • • • • • nz • • • •
Suitable cleaning Spirit Spirit Spirit Spirit Spirit White Water Solvent Water BTI foam Petrol, Water Water
agent**
spirit
cleaner dilution
* Definition according to DIN 52452, part 4 1* Gray tones with fungicidal properties