02 - BTI - We know your business

1006
BONDING + SEALING
�����
Sealing compound SI-A
High grade, permanently elastic 1-component silicone acetate sealing component
g Verified quality
Meets the requirements of DIN 18545, part 2, group E
g Excellent durability
Resistant to aggressive; non-aging and UV-resistant;
coating compatible*, can not be coated over*;
elastic even in extreme climatic conditions
* Terms acc. to DIN 52452, part 4
Range of application:
Glass sealing acc. to DIN 18545, part 2, group E; joint
gaps in doors and windows; sealing glass components
and tiles; joints in kitchens
Processing instructions:
When gluing to surfaces ensure they are clean, dry, stable
and free of grease. For strongly absorbent surfaces
such as porous concrete pre-coating with S400 primer
(item no. 011521) is recommended. Smooth sealing
compound with BTI smoothing agent (item no. 001880).
Tools can be cleaned immediately after use with white
spirit. Risk of corrosion and oxidation on metals such as
copper, aluminum, lead and zinc surfaces.
Technical data
(bei +20 °C/55 % relative humidity)
Usage temperature +1 °C to +30 °C
Skin building time 10 – 15 min
Curing 2 mm/24 hrs
Shore A hardness 20 ±5
Temperature stability -50 °C to +150 °C
Max. permitted permanent movement absorption 25 %
Joint width min. 5 mm to max. 30 mm
Storage 12 months
Item Unit Color Container Content
number Pieces ml
358169 1/24 transparent cartridge 310
358177 1/24 white cartridge 310
358185 1/12 gray cartridge 310
358215 1/12 oak cartridge 310
358207 1/12 dark brown cartridge 310
358193 1/12 black cartridge 310
08-140 A/P/T 08140
Item Unit Color Container Content
number Pieces ml
304867 12 transparent tube 410
304891 12 white tube 410
304875 12 transparent tube 580
08-141 A/P/T 08141
The details specified in this publication are based on our current knowledge and experience. Due to the abundance of possible processing and application influences this information does not release the processor from performing his
own tests and trials. Legally binding assurance of certain characteristics or suitability for a concrete implementation objective can not be derived from this information.