1006
BONDING + SEALING
�����
Duo Fast OZR
2K polyurethane foam for quick and permanent fixing of door frames
g High operational security
Secure activation, constant foam quality through
solid valve technology, no re-pressing after reaching
the spreading time
g Secure installation
Very good adhesion on nearly all surfaces common in
construction, curing is independent of air humidity
Range of application:
For door frame installation; to fill and build up joint
gaps in windows, window sills, roller shutter housings,
bath and shower tubs, etc.; filling wall breakthroughs
and cavities, to fix switching cabinets and insulation
boards
Processing instructions:
Open protection on activation top and pull activation
top with the wire as far as possible. Snap the wire at
the intended break above the valve and screw the valve
in the angle adapter. Shake the can hard and emerge
the foam with the valve pointing down. Joint must not
be more than half filled. The can contents must be
processed after activation within the pot time, as the
foam will otherwise cure in the can causing a risk of
bursting. Do not activate cans above temperatures of
+25 °C (risk of bursting).
Technical data
(at +23 °C/50% rel. air humidity)
Yield foamed free approx. 13 l
Foam expansion 200 – 300 %
Can temperature max. +25 °C
Surface temperature min. +10 °C
Adhesive-free after approx. 8 min
Sliceable after approx. 15 min
Spreadable/strainable after approx. 1 h
Pot time at +10 °C 8 min
Pot time at +20 °C 5 min
Pot time at +25 °C 3 min
Shelf life at +20 °C 9 months
Item Unit Color Container content
number Pieces ml
004603 12 light blue can 400
08-657 A/P/T 08567AA
The details specified in this publication are based on our current knowledge and experience. Due to the abundance of possible processing and application influences this information does not release the processor from performing his
own tests and trials. Legally binding assurance of certain characteristics or suitability for a concrete implementation objective can not be derived from this information.
WWW.bTI-gROUP.COM