Materiali e Tecnologie per la realizzazione di sostituti - FedOA ...

92 - CAPITOLO 4
Tipo
PCL/DMAc PCL/NaCl PCL/HA
(wt/wt) (v/v) (wt/wt) (v/v) (wt/wt) (v/v)
Compressione
(1kg-1h)
B40 20/80 17/83 100/0 100/0 71/29 87/13 No 55
B70 20/80 17/83 100/0 100/0 59/41 80/20 No 55
B100 20/80 17/83 100/0 100/0 50/50 74/26 No 55
HA40 20/80 17/83 5/95 09/91 71/29 87/13 Si 55
HA70 20/80 17/83 5/95 09/91 59/41 80/20 Si 55
HA100 20/80 17/83 5/95 09/91 50/50 74/26 Si 55
Tabella 16: Scaffold macroporosi in PCL con HA realizzati mediante phase inversion e phase
inversion/salt leaching
Tipo
PCL/(THF/DMSO) PCL/NaCl PCL/Hyaff11 THF/DMSO
(wt/wt) (v/v) (wt/wt) (v/v) (wt/wt) (v/v) (wt/wt) (v/v)
PHS1 20/80 17/83 5/95 09/91 100/0 100/0 80/20 83/17
PHS1 20/80 17/83 5/95 09/91 90/10 91/09 80/20 83/17
PHS2 20/80 17/83 5/95 09/91 80/20 82/18 80/20 83/17
PHS3 20/80 17/83 5/95 09/91 70/30 77/23 80/20 83/17
PHS4 20/80 17/83 5/95 09/91 80/20 91/09 50/50 55/45
Tabella 17: Scaffold macroporosi in PCL con Hyaff11 ® realizzati per phase inversion/salt
leaching
Successivamente si riportano le tabelle relative alle diverse tipologie di scaffold
macroporosi in PCL rinforzati con fibre di PLLA realizzati mediante tecnica di
solvent casting/salt leaching al variare dei rapporti ponderali tra matrice e fibra,
dell’ammontare di NaCl e della presenza di ulteriori sistemi di rinforzo di tipo
particellare (α-TCP):
Tipo
PCL/DMAc PCL/NaCl PCL/PLLA
(wt/wt) (v/v) (wt/wt) (v/v) (wt/wt) (v/v)
T
(°C)
TCP0A 10/90 17/83 10/90 18/82 82/18 84/16 25
TCP0B 15/85 17/83 10/90 18/82 82/18 84/16 25
TCP0C 20/80 17/83 10/90 18/82 82/18 84/16 25
Tabella 18: Scaffold macroporosi di PCL rinforzati con fibre di PLLA realizzati mediante phase
inversion/ salt leaching;
T
(°C)