Metallphysik Dienstag<br />
M 14.3 Di 10:45 H6<br />
A nanoindentation study of the effect of crystal-size on shear<br />
banding in Mg-based nanophase composites — •Shantanu<br />
Madge 1 , Gerhard Wilde 1 , and Lindsay Greer 2 — 1 Institute<br />
of Nanotechnology, Forschungszentrum Karlsruhe, D-76021, Germany.<br />
— 2 Department of Materials Science and Metallurgy, University of<br />
Cambridge, Cambridge CB2 3QZ, U.K.<br />
Nanoindentation has been used to study the efficacy of crystals in obstructing<br />
shear band propagation in two nanophase composites obtained<br />
by partial devitrification of Mg-based bulk metallic glasses. Pronounced<br />
steps are observed in the loading curves for the as-cast glasses, which reflect<br />
shear banding in the material. The composition Mg65Cu15Ag10Y10<br />
(at. effective in blocking shear band propagation in the partly crystallized<br />
material. On the other hand, the glass Mg66Ni20.4Nd13.6 (at. crystals<br />
that are much coarser and consequently, are more effective in blocking<br />
shear band propagation. The implications of these results for optimising<br />
the mechanical properties of bulk glasses are discussed.<br />
M 14.4 Di 11:00 H6<br />
Widerstand, Thermokraft und Struktur amorpher Al100−xTix-<br />
Legierungen — •Jan Werner 1 , Inna Plyushchay 2 und Peter<br />
Häussler 1 — 1 TU Chemnitz, 09107 Chemnitz — 2 Taras Shevchenko<br />
University, 03022 Kiew, Ukraine<br />
Al-ÜM-Legierungen mit frühen ÜM (Sc, Ti, V, Cr) haben hochinteressante<br />
Eigenschaften bezüglich des elektronischen Transports, z.B. drastische<br />
Veränderungen des Temperaturkoeffizienten des Widerstand bei<br />
mittleren Temperaturen, sie können Memory-Effekte zeigen und sind als<br />
amorphe Legierungen sehr stabil. Wir stellen solche Legierungen in situ<br />
bei T= 4K unter HV-Bedingungen zunächst amorph her und tempern<br />
die Proben dann bis in den kristallinen Zustand.<br />
M 15 Phasenumwandlungen III<br />
Es wird die statische Struktur durch Elektronenbeugung, der spezifische<br />
Widerstand und die Thermokraft jeweils als Funktion der Temperatur<br />
und der Zusammensetzung gemessen.<br />
Die Ergebnisse dieser Legierung mit einem frühen ÜM sollen mit Vorhersagen<br />
eines allgemeineren Modells für Al-ÜM-Legierungen, welches<br />
durch Messungen der Legierungen Al100−x ÜMx (Mn, Fe, Co, Ni) bestätigt<br />
wurde, verglichen werden. Die Struktureigenschaften und das Transportverhalten<br />
werden als Ergebnis optimierter Resonanzen zwischen dem<br />
Elektronensystem und der statischen Struktur mit Konsequenzen für die<br />
Phasenstabilität und den Transport diskutiert.<br />
M 14.5 Di 11:15 H6<br />
Widerstand und Struktur amorpher Al100−XNiX-Legierungen —<br />
•M. Lang, P. Häussler und J. Barzola — TU Chemnitz, Institut<br />
für Physik, D-09107 Chemnitz<br />
Amorphe Aluminium-Legierungen mit späten Übergangsmetallen<br />
(Mn, Fe, Co, Ni) haben in der Vergangenheit gezeigt, dass sie durch<br />
Hybridisierungseffekte zwischen den Al-p- und den unbesetzten<br />
ÜM-d-Elektronen ihre effektive Valenz derart variieren können,<br />
dass der Durchmesser der Fermikugel gerade so großist, dass er die<br />
Pseudobrillouin-Zone berühren kann. Es tritt ein die Phase stabilisierendes<br />
Pseudogap in der elektronische Zustandsdichte auf, das zusätzlich<br />
zu Transportanomalien führt.<br />
Die hier vorgestellten Schichten werden insitu bei 4K hergestellt, mittels<br />
Elektronenbeugung bzgl. der atomaren Struktur, sowie durch Messung<br />
des spezifischen Widerstandes charakterisiert.<br />
Die Struktureigenschaften und das Transportverhalten werden als Ergebnis<br />
optimierter Resonanzen zwischen dem Elektronensystem und der<br />
statischen Struktur, zusammen mit anderen Al-ÜM-Legierungen, diskutiert.<br />
Zeit: Dienstag 11:45–12:45 Raum: H16<br />
M 15.1 Di 11:45 H16<br />
Temperature dependence of lattice misfit in a creep deformed<br />
single crystal superalloy using synchrotron X-radiation —<br />
•Weiye Chen 1 , Nora Darowski 2 , Ivo Zizak 2 , Gerhard Schumacher<br />
2 , Nelia Wanderka 2 , Hellmuth Klingelhoeffer 3 , and<br />
Wolfgang Neumann 1 — 1 Humboldt-Universitaet zu Berlin, Institut<br />
fuer Physik — 2 Hahn-Meitner-Institut Berlin, Bereich Strukturforschung<br />
— 3 Bundesanstalt fuer Materialforschung und -pruefung Berlin<br />
At high temperatures the application of an external load can lead to<br />
directional growth (gamma prime rafting) of gamma prime precipitates<br />
in single crystal superalloys. The lattice misfit between the gamma prime<br />
precipitates and the gamma matrix is one of the parameters which determine<br />
the kinetics and morphology of the gamma prime rafts. In the<br />
present study the gamma/gamma prime lattice mismatch in specimens<br />
of single crystal superalloy SC16 creep deformed at 1223 K and 150 MPa<br />
to a creep strain of 0.5 means of X-ray diffraction using synchrotron<br />
radiation. The measurements have been performed between room temperature<br />
and 1173 K in the both directions parallel and perpendicular<br />
to the [001] load axis. At room temperature the gamma/gamma prime<br />
lattice mismatch measured on the (002) reflection has a positive sign<br />
and is larger compared to the mismatch in the non-deformed specimen,<br />
while the mismatch measured on the (200) reflection is slightly negative<br />
and its value is smaller than that of the non-deformed specimen.<br />
In both directions the gamma/gamma prime lattice mismatch decreases<br />
with increasing temperature.<br />
M 15.2 Di 12:00 H16<br />
Phase transition of Ni12at.%Al by plastic deformation —<br />
•Peter Drechsler 1 and Ferdinand Haider 2 — 1 Abteilung für<br />
Funktionswerkstoffe der Medizin und Zahnheilkunde, Universität<br />
Würzburg, Pleicherwall 2, 97070 Würzburg — 2 Lehrstuhl für Experimentalphysik<br />
I, Universität Augsburg, Universitätsstraße 1, 86159<br />
Augsburg<br />
The cyclic behavior of the stress response of polycrystalline Ni12at.%Al<br />
under lcf loading at mean plastic strain rates between 10 −3 1/s and<br />
10 −1 1/s and temperatures between 298K and 773K shows after the inital<br />
hardening caused by the nucleation of psb either further hardening or<br />
saturation and softening. The behavior of the flow stress can be related<br />
to the particle size of the γ ′ -precipitates as tem investigation revealed.<br />
Depending on strain rate and temperature one can distinguish two ranges<br />
in which the average radius of the precipitates shrinks or grows. This effekt<br />
can be simulated by means of a model, that includes the shrinking of<br />
the precipitates by dislocation cutting as well as the deformation induced<br />
accelerated diffusion for the growth of the particles. The calculated values<br />
for the diffusion coefficient agree with values of Militizer et al. for the<br />
deformation induced vacancy production. The model predicts the values<br />
of the radii of the precipitates qualitatively and quantitatively. The tem<br />
investigation and the model clearly show the two ranges of shrinking<br />
and growth. The average particle grows with increasing temperature and<br />
decreasing strain rate.<br />
M 15.3 Di 12:15 H16<br />
Structural transformations in AS21X alloy — •Miloˇs Janeček,<br />
Torbjørn Lamark und Juri Estrin — Institut für Werkstoffkunde<br />
und Werkstofftechnik, TU Clausthal, Agricolastr. 6, 38678 Clausthal-<br />
Zellerfeld<br />
The evolution of precipitation processes in a commercial magnesium<br />
alloy AS21X was studied using transmission electron microscopy (TEM),<br />
electron diffraction and energy dispersive X–ray analysis. Three different<br />
states, namely the as cast state and two annealed states after 1000 and<br />
2000 hours, were selected for the investigation of precipitation processes<br />
in this alloy. Furthermore, it was demonstrated by TEM analysis that<br />
twinning is the predominant deformation mechanism in this alloy under<br />
the conditions studied.<br />
M 15.4 Di 12:30 H16<br />
Charakterisierung der Frühstadien der Entmischung in<br />
binären Legierungen mit der radialen Verteilungsfunktion<br />
— •Alexander Heinrich, Talaat Al-Kassab und Reiner<br />
Kirchheim — Institut für Materialphysik, Tammanstraße 1, 37077<br />
Göttingen<br />
Die Systeme Cu0.7at.%Fe und Cu2.0at.%Co wurden mit dem Feldionenmikroskop<br />
(FIM) und der der Tomographischen Atomsonde (TAP)<br />
untersucht. Proben von Cu-Co wurden dabei für Zeiten von einigen Stunden<br />
bis 15 min bei 853 K und 703 K ausgelagert, Proben von Cu-Fe für<br />
Zeiten von 16h bis 15 min bei 803 K und 703K.<br />
Besonderes Augenmerk der Analysen gilt hierbei den Frühstadien der<br />
Keimbildung. Ein neues Auswerteverfahren zur Charakterisierung der